Professional one-component material for industrial use for hydrophobization of asphalt concrete and cement concrete pavements of airfields and highways, pavement pavements, structures of buildings and structures
Hydrophobization of asphalt concrete and cement concrete pavements of airfields and highways, structures of buildings and structures (cement concrete tiles, natural stone, paving stones, etc.). The composition is resistant to washing out by atmospheric precipitation and the effects of reagents, does not stain or change the texture of the coating, does not reduce the adhesion coefficient and allows operation immediately after application.
Advantages
High penetrating ability, resistance of the finished layer to aggressive environmental conditions.
Reliable filling of pores and cracks with a width of not more than 0.5 mm.
An effective method to prevent corrosion of concrete structures.
High adhesion to building materials.
Simple unified application technology.
Composition
Transparent solution of organosilicon compounds and rheological modifiers in an organic solvent (STO 77310225.005-2015).
Specifications
Mass fraction of non-volatile substances, %, not less than: 12 Density at (+20 ± 0.5) ºС, g/cm3: 0.8 ± 0.05 Relative viscosity according to VZ-246 viscometer at temperature (+20 ± 0.5 ) ºС, s, not less than: 8 Complete drying time (+20 ± 0.5) ºС, h, not more than: 0.5
Technology
To clear a surface of pollution.
Carry out the treatment with Brit penetrating impregnation by pneumatic spraying or manually with a roller or brush.
Drying time depending on climatic factors - from 15 to 45 minutes. For porous and absorbent coatings, a second coat after one hour is recommended.
The operation of airfield and road surfaces is permissible no earlier than one hour after the completion of the treatment with Brit penetrating impregnation.